@article{oai:ynu.repo.nii.ac.jp:00003995,
 author = {Lu, Hui and Li, Chunxia and Yin, Fuxing and Fang, Qianfeng and Umezawa, Osamu},
 issue = {8},
 journal = {Metallurgical and materials transactions. A, Physical metallurgy and materials science},
 month = {Aug},
 note = {application/pdf, Effects of Fe addition on the oxygen diffusion and the Snoek-type relaxation damping behavior of the Ti-15 wt pct Mo alloy were investigated in this study. After surface oxidation treatment, the Ti-15 wt pct Mo-1 wt pct Fe alloy exhibits a higher damping capacity compared to the Ti-15 wt pct Mo alloy. The dual-phase zone and the oxygen-enriched β-phase zone in the surface-oxidation-treated Ti-Mo alloys were determined by electron backscattered diffraction (EBSD) and hardness measurements. Based on the oxygen distributions in both alloys obtained through a diffusion model, the relative damping capacity of different zones contributing to the beam sample damping was estimated to be proportional to the thickness of the oxygen dissolved zones. On the other hand, the substitutional solute of Fe in the Ti-Mo-Fe alloy is considered to affect the oxygen distribution by lengthening the oxygen diffusion zone and increasing the oxygen concentration in this zone. As a result, the addition of Fe in Ti-Mo alloy improves the damping capacity of the surface-oxidation-treated alloys.},
 pages = {2242--2249},
 title = {Effects of Fe addition on the snoek-type damping behavior of surface-oxidation-treated Ti-Mo alloys},
 volume = {42},
 year = {2011}
}