{"_buckets": {"deposit": "29e575a5-7f92-4b29-8c8e-de402cdcfd95"}, "_deposit": {"created_by": 3, "id": "10361", "owners": [3], "pid": {"revision_id": 0, "type": "depid", "value": "10361"}, "status": "published"}, "_oai": {"id": "oai:ynu.repo.nii.ac.jp:00010361", "sets": ["496"]}, "author_link": ["480", "36731", "36733", "36730", "36732", "36734"], "item_2_biblio_info_8": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2019-07", "bibliographicIssueDateType": "Issued"}, "bibliographicPageEnd": "69", "bibliographicPageStart": "64", "bibliographicVolumeNumber": "810", "bibliographic_titles": [{"bibliographic_title": "Key Engineering Materials"}]}]}, "item_2_description_5": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "Quasi-cleavage facets have been detected in the stress corrosion cracking fracture of type 304 and type 316 austenitic stainless steels under an environment containing chloride. Their morphology and crystal orientation were analyzed. In both steels the cold-worked material (CW) showed higher crack propagation rate than annealed one (ST), where the variation of the propagated crystal planes of the CW was higher than that of the ST, and the {111} facet was detected in the CW. Then the CW reveals higher possibilities to choose a low energy crack path rather than the ST. The rearrangement and multiply of {111} dislocation arrays may introduce the {111} transgranular cracking in the CW, and the combining duplex {111} slip operations may result in the {110} facet.", "subitem_description_type": "Abstract"}]}, "item_2_publisher_35": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "Scientific.net"}]}, "item_2_relation_13": {"attribute_name": "DOI", "attribute_value_mlt": [{"subitem_relation_type_id": {"subitem_relation_type_id_text": "10.4028/www.scientific.net/KEM.810.64", "subitem_relation_type_select": "DOI"}}]}, "item_2_relation_44": {"attribute_name": "関係URI", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "https://doi.org/10.4028/www.scientific.net/KEM.810.64"}], "subitem_relation_type_id": {"subitem_relation_type_id_text": "https://doi.org/10.4028/www.scientific.net/KEM.810.64", "subitem_relation_type_select": "DOI"}}]}, "item_2_source_id_9": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "16629795", "subitem_source_identifier_type": "ISSN"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "metadata only access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_14cb"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "Wakinaga, Ryo"}], "nameIdentifiers": [{"nameIdentifier": "36730", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Koga, Norimitsu"}], "nameIdentifiers": [{"nameIdentifier": "36731", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Umezawa, Osamu"}], "nameIdentifiers": [{"nameIdentifier": "480", "nameIdentifierScheme": "WEKO"}, {"nameIdentifier": "20343171", "nameIdentifierScheme": "e-Rad", "nameIdentifierURI": "https://kaken.nii.ac.jp/ja/search/?qm=20343171"}]}, {"creatorNames": [{"creatorName": "Morita, Motoaki"}], "nameIdentifiers": [{"nameIdentifier": "36732", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Motoda, Shinichi"}], "nameIdentifiers": [{"nameIdentifier": "36733", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Shinohara, Tadashi"}], "nameIdentifiers": [{"nameIdentifier": "36734", "nameIdentifierScheme": "WEKO"}]}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Austenitic Stainless Steel", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Cold-Work", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Corrosion Pitting", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Electron Backscattering Diffraction", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Quasi-Cleavage Fracture", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Stress Corrosion Cracking", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Transgranular Cracking", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "Crystal Orientation Analysis on Stress Corrosion Cracking Facets in Austenitic Stainless Steels", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Crystal Orientation Analysis on Stress Corrosion Cracking Facets in Austenitic Stainless Steels"}]}, "item_type_id": "2", "owner": "3", "path": ["496"], "permalink_uri": "http://hdl.handle.net/10131/00013023", "pubdate": {"attribute_name": "公開日", "attribute_value": "2020-03-05"}, "publish_date": "2020-03-05", "publish_status": "0", "recid": "10361", "relation": {}, "relation_version_is_last": true, "title": ["Crystal Orientation Analysis on Stress Corrosion Cracking Facets in Austenitic Stainless Steels"], "weko_shared_id": -1}
Crystal Orientation Analysis on Stress Corrosion Cracking Facets in Austenitic Stainless Steels
http://hdl.handle.net/10131/00013023
http://hdl.handle.net/10131/00013023565807ee-98f2-4544-89e0-c5cfa20f8427
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2020-03-05 | |||||
タイトル | ||||||
タイトル | Crystal Orientation Analysis on Stress Corrosion Cracking Facets in Austenitic Stainless Steels | |||||
言語 | ||||||
言語 | eng | |||||
キーワード | ||||||
主題 | Austenitic Stainless Steel, Cold-Work, Corrosion Pitting, Electron Backscattering Diffraction, Quasi-Cleavage Fracture, Stress Corrosion Cracking, Transgranular Cracking | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
資源タイプ | journal article | |||||
アクセス権 | ||||||
アクセス権 | metadata only access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_14cb | |||||
著者 |
Wakinaga, Ryo
× Wakinaga, Ryo× Koga, Norimitsu× Umezawa, Osamu× Morita, Motoaki× Motoda, Shinichi× Shinohara, Tadashi |
|||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | Quasi-cleavage facets have been detected in the stress corrosion cracking fracture of type 304 and type 316 austenitic stainless steels under an environment containing chloride. Their morphology and crystal orientation were analyzed. In both steels the cold-worked material (CW) showed higher crack propagation rate than annealed one (ST), where the variation of the propagated crystal planes of the CW was higher than that of the ST, and the {111} facet was detected in the CW. Then the CW reveals higher possibilities to choose a low energy crack path rather than the ST. The rearrangement and multiply of {111} dislocation arrays may introduce the {111} transgranular cracking in the CW, and the combining duplex {111} slip operations may result in the {110} facet. | |||||
書誌情報 |
Key Engineering Materials 巻 810, p. 64-69, 発行日 2019-07 |
|||||
ISSN | ||||||
収録物識別子タイプ | ISSN | |||||
収録物識別子 | 16629795 | |||||
DOI | ||||||
識別子タイプ | DOI | |||||
関連識別子 | 10.4028/www.scientific.net/KEM.810.64 | |||||
出版者 | ||||||
出版者 | Scientific.net | |||||
関係URI | ||||||
識別子タイプ | DOI | |||||
関連識別子 | https://doi.org/10.4028/www.scientific.net/KEM.810.64 | |||||
関連名称 | https://doi.org/10.4028/www.scientific.net/KEM.810.64 |